氧化法熔铸AZS41#
含有更多分布均匀的氧化锆结 晶体，具有极强的璃液侵蚀性能。因比应用于玻璃熔窑与玻璃液接触部位，如:电极孔、窑坎、流液洞、拐角转、熔化部池壁等。
- 18503811656
理化指标
| AZS-41# | |
| SiO₂ |
≤13 |
| Al₂O₃ | 余量 remain |
| ZrO₂ | 40-44 |
| Na₂O | ≤1.3 |
| Fe₂O₂ + TiO₂ + CaO + Na₂O | ≤2.5 |
| 玻璃相渗出温度 exudation temperature of glass phase | ≥1410 |
| 0.2Pa下荷重软化温度 refractoriness under load of 0.2MPa(℃) | ≥1700 |
| 抗玻璃液侵蚀 anti-corrosion rate of glass liquid (1500℃36hr,普通玻璃ordinary glass)mm/24hr | ≤1.3 |
| 气泡析出率 bubbling tendency(1300°、10hr,普通玻璃 ordinary glass)% | ≤1.0 |
| 容量 density (g/cm3)普通浇铸 normal casting 倾斜浇铸 tilt casting | ≥3.55 |
| 准无缩孔浇铸 end cut | ≥3.85 |
| 无缩孔浇铸 void-free casting | ≥3.95 |