Products & Service
产品服务
氧化法熔铸AZS36#
抗碱飞灰和碱蒸汽性能优于 AZS33、抗蠕变性能强。主要用于强烈侵蚀的上部结构，也可用于接触玻璃液部位
理化指标
| AZS-36# | |
| SiO₂ |
≤14 |
| Al₂O₃ | 余量 remain |
| ZrO₂ | 35-40 |
| Na₂O | ≤1.5 |
| Fe₂O₂ + TiO₂ + CaO + Na₂O | ≤2.5 |
| 玻璃相渗出温度 exudation temperature of glass phase | ≥1400 |
| 0.2Pa下荷重软化温度 refractoriness under load of 0.2MPa(℃) | ≥1700 |
| 抗玻璃液侵蚀 anti-corrosion rate of glass liquid (1500℃36hr,普通玻璃ordinary glass)mm/24hr | ≤1.4 |
| 气泡析出率 bubbling tendency(1300°、10hr,普通玻璃 ordinary glass)% | ≤1.4 |
| 容量 density (g/cm3)普通浇铸 normal casting 倾斜浇铸 tilt casting | ≥3.5 |
| 准无缩孔浇铸 end cut | ≥3.7 |
| 无缩孔浇铸 void-free casting | ≥3.8 |